Submit a Project Contact Us

ASB Industries: Innovative Industrial Coating Services

ASB Industries’ industrial coating services can dramatically improve your equipment’s performance and extend its working life. We offer turnkey thermal spray and cold spray coatings, as well as secondary services like welding, machining, and grinding, to give our customers finished, ready-to-use treated parts.

With decades of experience in identifying the causes of wear, we can adapt our thermal spray and cold spray surfacing technologies to best address the needs of your application.

Featured Applications
  • ASB is Working in all Areas of our Production
    (Mar 25, 2020)
    ASB Industries is currently in full production in all areas of our company.  Ohio, USA has very strict rules which ASB is following these guidelines.  We have been notified by many of our customers of their operations as Essential Business which ASB is part of processing equipment components. We greatly understand the impact of this challenge affecting all of us.

    Upgrade to our Cold Spray Nitrogen Gas System
    (Feb 13, 2020)

    Nitrogen High Pressure Builder for Cold Spray

    The main process gas for cold spraying is nitrogen. Critical particle velocity is required for physical build-up--


First-Class Industrial Coating Services

With advanced equipment, a skilled staff of thermal sprayers and machinists, and extensive machining and grinding capabilities, ASB can provide unique thermal spray and cold spray solutions for extreme wear, high temperature barriers, and all-encompassing part repair.

Our in-house, turnkey industrial coating services will give your equipment extended service life by meeting or exceeding original equipment designs. Submit your project or contact ASB Industries today!

Feb 3, 2020

Thermal Spray Conference Presentation In June 2020

Cold Spray Corrosion Study

The following Abstract describes an upcoming presentation by ASB's Dr. M. Daroonparvar at the ITSC in June located in Vienna. Current cold sprayed commercially pure (CP)-Al coatings on Mg alloys lack--

Category: Current News
Posted by: charlie
Applying Protective Double Layered Coatings on Magnesium Alloys Using High Pressure Cold Spray Process
M. Daroonparvar, Charles. M. Kay, Rajeev Kumar GuptaResearch and Development Department, ASB Industries. Inc, Barberton, Ohio-44203, United States of America. 2Department of Chemical and Biomilecular Engineering, Corrosion Engineering Program, The University of Akron, Akron, Ohio-44325, United States of America.
Current cold sprayed (N2 as propellant gas) commercially pure (CP)-Al coatings on Mg alloys lack acceptable hardness, wear resistance and are highly susceptible to localized corrosions in chloride containing solutions. Hence, commercially pure α-Ti layer with high passivation propensity (with about 1293.05mV vs. SCE trans-passive potential), hardness and low wear rate was applied on the CP-Al coated Mg alloy. Titanium layer deeply penetrated into Al layer with heavily deformation.
This was accompanied by noticeable densification of softer underneath layer (Al) by hard particles (Ti) with high kinetic energy (hammering effect). Titanium layer raised micro-hardness (HV0.025) from 56.43 (CP-Al coated Mg alloy) to 263.03 for Ti/Al coated Mg alloy. The surface with higher hardness i.e. Ti/Al coating provides lower wear rate followed by Mg bulk and Al coating surfaces, respectively. It should be noted that further studies (long-term corrosion tests) are mandatory to elucidate the effectiveness and corrosion protection performance of cold sprayed double layer coatings on Mg alloys.
Cold Spray Characterization Study